The melamine impregnated paper laminated through high pressure & heat with different embossed press plates onto substrate like Particle Board, MDF, OSB & plywood, which are mainly for knock-down furniture industry, examples: kitchen cabinet, office furniture, furniture component or having apply to the built-in work such as partition, wall and counter.

The melamine faced enhance their resistance to scratches, moisture, and chemicals.

The Panels Enhance

Thus ideal materials for furniture applications ranging from residential decorations responding to every design needs

The melamine impregnated paper laminated through high pressure & heat with different embossed press plates onto substrate like Particle Board, MDF, OSB & plywood, which are mainly for knock-down furniture industry, examples: kitchen cabinet, office furniture, furniture component or having apply to the built-in work such as partition, wall and counter.

The melamine faced enhance their resistance to scratches, moisture, and chemicals.

The Panels Enhance

Thus ideal materials for furniture applications ranging from residential decorations responding to every design needs

Standard

4×8 ft., 6×8 ft., 7×9 ft., 6×12 ft.

Thickness

8-38 mm

Main items (mm.)
8, 9, 12, 15, 16, 25, 30 and 36
(Other thickness are upon request)

Class

E2, E1, E0, SE0,
HMR-E2, HMR-E1,
CARB P2

MELAMINE TESTING

Abrasion Resistance
Taber abrader applied at 60 rpm on sample surface (100×100 mm.), Insignificant reduction of sample weight.

Burning Resistance
Sample is placed in oven at 70 degree Celsius for 24 hours, No cracks.

Steam Resistance
Sample surface exposed for 1 hour to steam. Slightly change in gloss/color.

Acid Test
Sample surface exposed to 0.2 N&4 N Hydrochloric acid respectively for 15 minutes and 24 hours testing. Slightly change in gloss/color.

Cracking Resistance
Sample is placed in oven at 70 degree Celsius for 24 hours, No cracks.

Dry Heat Resistance
A vessel containing oil at 180 degree Celsius placed on sample surface, Slightly change in gloss/color.

Stain Resistance
Sample surface exposed to various staining materials for 16 hours. Staining materials:coffee,tea,soy sauce,acetone,etc., No visible change.

Porosity
Graphite laid on sample surface, No graphite stain observed with naked eyes.